Polyethylene films having high resistance to deformation or elgonation

ABSTRACT

Disclosed is a method for producing polyethylene films which have high resistance to deformation or elongation under loading in tension. The method comprises orienting in the machine direction (MD) a high density polyethylene film at a drawdown ratio effective to give the film an MD tensile strength at yield greater than or equal to 50,000 psi, wherein the HDPE has a density greater than 0.940 g/cm 3 .

FIELD OF THE INVENTION

The invention relates to polyethylene films. More particularly, the invention relates to polyethylene films which have high resistance to deformation or elongation under loading in tension.

to BACKGROUND OF THE INVENTION

Polyethylene is divided into high-density (HOPE, density 0.941 g/cm³ or greater), medium-density (MOPE, density from 0.926 to 0.940 g/cm³), low-density (LDPE, density from 0.910 to 0.925 g/cm³), and linear low-density polyethylene (LLDPE, density from 0.910 to 0.925 g/cm³). See is ASTM 04976-98: Standard Specification for Polyethylene Plastic Molding and Extrusion Materials. Polyethylene can also be divided by molecular weight. For instance, ultra-high molecular weight polyethylene denotes those which have a weight average molecular weight (Mw) greater than 3,000,000. See U.S. Pat. No. 8,265,504. High molecular weight polyethylene usually includes those which have an Mw from 130,000 to 1,000,000.

One of the main uses of polyethylene (HOPE, LLDPE, and LOPE) is in film applications, such as grocery sacks, institutional and consumer can liners, merchandise bags, shipping sacks, food packaging films, multi-wall bag liners, produce bags, deli wraps, stretch wraps, and shrink wraps. The key physical properties of polyethylene film include tear strength, impact strength, tensile properties, stiffness and transparency. Tensile properties are an important indicator of the material's behavior under loading in tension. Tensile properties include tensile strength at yield, tensile strength at break (ultimate tensile strength), tensile modulus (Young's modulus), and elongation at yield and break. High tensile strength at yield is required for heavy duty bags such as those for trash, top soil, and fertilizer. High tensile strength at yield means high resistance to deformation or elongation under loading.

Machine direction orientation (MDO) is known to the polyolefin industry. When a polymer is strained under uniaxial stress, the orientation becomes aligned in the direction of pull. For instance, U.S. Pat. No. 6,391,411 teaches the MDO of very high molecular weight (both Mn and Mw greater than 1,000,000) HDPE films. However, MDO of very high molecular weight HDPE films are limited because these films are difficult to stretch to a high draw-down ratio.

Polyethylene films, although having many desirable properties for the use in heavy duty bags, have low tensile strength at yield. Imagine that a person carries a 50-pound trash bag, while the bag elongates to five-foot long. She or he will feel unsafe and inconvenient. It would be desirable to prepare a polyethylene film which, along with other properties, has high tensile strength at yield so that the film can be used for heavy duty bags.

SUMMARY OF THE INVENTION

The invention is a method for preparing a polyethylene film which has high resistance to deformation or elongation under load in tension. The method comprises orienting in the machine direction (MD) a high density polyethylene (HDPE) film at a draw-down ratio effective to give the film an MD tensile strength at yield greater than or equal to 50,000 psi. The HDPE has a density greater than 0,940 g/cm³. Preferably, the HDPE has a density within the range of 0.950 to 0.965 g/cm³, a weight average molecular weight (Mw) within the range of 130,000 to 1,000,000, and a number average molecular weight (Mn) within the range of 10,000 to 500,000.

DETAILED DESCRIPTION OF THE INVENTION

Tensile properties are an important indicator of the material's behavior under loading in tension. Tensile properties include tensile strength at yield, tensile strength at break (ultimate tensile strength), tensile modulus (Young's modulus), and elongation at yield and break. Tensile strength at yield is the maximum stress at which permanent, non-elastic deformation begins. Yield point is the point (load) at which the material yields, i.e., increase in strain occurs without an increase in stress. Ultimate tensile strength is the maximum stress a material can withstand before failing.

Elongation at yield is the strain that the material undergoes at the yield point, or the percent change in length that occurs while the material is stressed to its yield point. Elongation at break is the strain at failure, or the percent change in length at failure. Tensile, or Young's modulus, is the ratio of stress to strain within the elastic region of the stress-strain curve (prior to the yield point).

The method of the invention provides polyethylene films having improved tensile properties. The method comprises orienting in the machine direction (MD) a high density polyethylene (HDPE) film at a draw down ratio effective to give the film an MD tensile strength at yield greater than or equal to 50,000 psi. Polyethylene resins suitable for making the HDPE film for the use in the invention have a density greater than 0.940 g/cm³, Preferably the density is within the range of about 0.941 to about 0.965 g/cm³. More preferably, the density is within the range of about 0.949 to about 0.959 g/cm³.

Preferably, the polyethylene resins have a number average molecular weight (Mn) within the range of about 10,000 to about 500,000, more preferably from about 11,000 to about 50,000, and most preferably from about 11,000 to about 20,000. Preferably, the polyethylene resin has a weight average molecular weight (Mw) within the range of about 130,000 to about 1,000,000, more preferably from about 150,000 to about 500,000, and most preferably from about 155,000 to about 250,000. Preferably, the polyethylene resin has a molecular weight distribution (Mw/Mn) within the range of about 5 to about 20, more preferably from about 7 to about 18, and most preferably from about 9 to about 17.

The Mw, Mn and Mw/Mn are obtained by gel permeation chromatography (GPC) on a Waters GPC2000CV high temperature instrument equipped with a mixed bed GPC column (Polymer Labs mixed B-LS) and 1,2,4-trichlorobenzene (TCB) as the mobile phase. The mobile phase is used at a nominal flow rate of 1.0 mL/min and a temperature of 145° C. No antioxidant is added to the mobile phase, but 800 ppm BHT is added to the solvent used for sample dissolution. Polymer samples are heated at 175° C. for two hours with gentle agitation every 30 minutes. Injection volume is 100 microliters.

is The Mw and Mn are calculated using the cumulative matching % calibration procedure employed by the Waters Millennium 4.0 software. This involves first generating a calibration curve using narrow polystyrene standards (PSS, products of Waters Corporation), then developing a polyethylene calibration by the Universal Calibration procedure.

Preferably, the polyethylene resins have a melt index MI₂ from about 0.03 to about 0.15 dg/min, more preferably from about 0.04 to about 0.15 dg/min, and most preferably from 0.05 to 0.10. The MI₂ is measured at 190° C. under 2.16 kg of pressure according to ASTM D-1238. In general, the higher the molecular weights, the lower the MI₂ values.

Preferably, the polyethylene resins are copolymers that comprise from about 90 wt % to about 98 wt % of recurring units of ethylene and from about 2 wt % to about 10 wt % of recurring units of a C₃ to C₁₀ α-olefin. Suitable C₃ to C₁₀ a-olefins include propylene, 1-butene, 1-pentene, 1-hexene, 4-methyl-1-pentene, and 1-octene, and the like, and mixtures thereof.

Suitable polyethylene resins can be produced by Ziegler catalysts or single-site catalysts. Ziegler catalysts are well known. Examples of suitable Ziegler catalysts include titanium halides, titanium alkoxides, vanadium halides, and mixtures thereof. Ziegler catalysts are used with cocatalysts such as alkyl aluminum compounds.

Single-site catalysts can be divided into metallocene and non-metallocene. Metallocene single-site catalysts are transition metal compounds that contain cyclopentadienyl (Cp) or Cp derivative ligands. For example, U.S. Pat. No. 4,542,199, the teachings of which are incorporated herein by reference, teaches metallocene catalysts. Non-metallocene single-site catalysts contain ligands other than Cp but have the same catalytic characteristics as metallocenes. The non-metallocene single-site catalysts may contain heteroatomic ligands, e.g., boraaryl, pyrrolyl, azaborolinyl or quinolinyl. For example, U.S. Pat. Nos. 6,034,027, 5,539,124, 5,756,611, and 5,637,660, the teachings of which are incorporated herein by reference, teach non-metallocene catalysts.

The polyethylene resins are converted into thick films by a high-stalk or in-pocket blown extrusion process. Both high-stalk and in-pocket processes are commonly used for making polyethylene films. The difference between the high-stalk process and the in-pocket process is that in the high-stalk process, the extruded tube is inflated a distance (i.e., the length of the stalk) from the extrusion die, while the extruded tube in the in-pocket process is inflated as the tube exits the extrusion die.

For instance, U.S. Pat. No, 4,606,879, the teachings of which are herein incorporated by reference, teaches high-stalk blown film extrusion apparatus and method. The process temperature is preferably within the range of about 150° C. to about 210° C. The thickness of the film is preferably within the range of about 3 to about 14 mils, more preferably within the range of about 6 to about 8 mils.

The blown films are then uniaxially stretched in the machine (or processing) direction to a thinner film. The ratio of the film thickness before and after orientation is called “draw-down ratio.” For example, when a 6-mil film is stretched to 0.6-mil, the draw-down ratio is 10:1. The draw-down ratio of the method of the invention is preferably greater than or equal to 7:1. More preferably, the draw-down ratio is greater than or equal to 10:1. Most preferably, the draw-down ratio is greater than or equal to 11:1.

During the MDO, the film from the blown-film line is heated to an orientation temperature. Preferably, the orientation temperature is between 60% of the difference between the glass transition temperature (Tg) and the melting point (Tm) and the melting temperature (Tm). For instance, if the blend has a Tg of 25° C. and a Tm of 125° C., the orientation temperature is preferably within the range of about 60° C. to about 125° C. The heating is preferably performed utilizing multiple heating rollers.

Next, the heated film is fed into a slow draw roll with a nip roller, which has the same rolling speed as the heating rollers. The film then enters a fast draw roll. The fast draw roll has a speed that is 2 to 10 times faster than the slow draw roll, which effectively stretches the film on a continuous basis.

The stretched film then enters annealing thermal rollers, which allow stress relaxation by holding the film at an elevated temperature for a period of time. The annealing temperature is preferably within the range of about 100° C. to about 125° C. and the annealing time is within the range of about 1 to about 2 seconds. Finally, the film is cooled through cooling rollers to an ambient temperature.

The invention includes the MD oriented (MDO) film made by the method. The MDO film has an MD tensile strength at yield greater than or equal to 50,000 psi. Tensile strength is tested according to ASTM D-882. Preferably, the MDO film has an MD tensile strength at yield greater than about 55,000 psi. Most preferably, the MDO film has an MD tensile strength at yield greater than about 69,000 psi.

Preferably, the MDO film has an MD Young's modulus greater than or equal to 500,000 psi. More preferably, the MD Young's modulus is greater than 900,000 psi. Most preferably, the MD Young's modulus is greater than 1,000,000 psi. Preferably, the MDO film has an MD tensile strength at break greater than 40,000 psi. More preferably, the MD tensile strength at break is greater than 50,000 psi. Most preferably, the MD tensile strength at break is greater than 55,000 psi.

Preferably, the MDO film has an MD elongation at yield is less than 25%. More preferably, the MD elongation at yield is less than 20%. Most preferably, the MD elongation at yield is less than 15%. Preferably, the MDO film has an MD elongation at break less than 50%. More preferably, the MD elongation at break is less than 25%. Most preferably, the MD elongation at break is less than 14%. Preferably, the MDO film has an MD elongation at yield which is essentially the same as the MD elongation at break.

The MDO film preferably remains at high transverse direction (TD) properties. Preferably, the MDO film has a TD Young's modulus greater than 300,000 psi; more preferably, greater than 350,000 psi. Preferably, the MDO film has a TD elongation at yield less than 4%, more preferably less than 3.5%. Preferably, the MDO film has a TD tensile strength at yield greater than 5,000 psi. Preferably, the MDO film has a TD elongation at break less than 400%, more preferably less than 300%. Preferably, the MDO film has a TD tensile strength at break greater than 3,500 psi.

The following examples merely illustrate the invention. Those skilled in the art will recognize many variations that are within the spirit of the invention and scope of the claims.

EXAMPLES 1-6 Machine Direction Orientation of High Density (0.959 g/cm³) High Stalk Polyethylene Films

A high density polyethylene (L5906, product of Equistar Chemicals, LP, MI₂: 0.057 dg/min, density: 0.959 g/cm³, Mn: 12,900, Mw: 207,000, and Mw/Mn: 16) is converted into films with a thickness of 6.0 mil on 200 mm the with 2 mm the gap. The films are produced at a stalk height of 8 die diameters and at blow-up ratios (BUR) of 4:1.

The films are then stretched into thinner films in the machine direction with draw-down ratios 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, and 11.6 in Examples 1-11, respectively. When the draw-down ratio is 1:1, the film is not oriented. The draw-down ratio of 11.6:1 is the maximum draw-down ratio limited by the orientation equipment and not the polymer film. The film properties are listed in Table 1. The data shows that as the films are oriented in the machine direction, the percent change in the difference between the MD break elongation % and MD yield elongation % relative to the unoriented film decreases to the point where the MD break elongation % is nearly identical to the MD yield elongation %. Similarly, as the draw-down ratio increases, the MD yield and break strengths substantially increase, indicating the film can withstand a significantly heavier load prior to both yielding (stretching) and breaking. A similar convergence in yield and break elongation %, but to a lesser degree, is seen in the transverse-direction properties of the films.

EXAMPLES 12-22 Machine Direction Orientation of High Density (0.959 g/cm³) In-pocket Polyethylene Films

Examples 1-11 are repeated, but the films are made at in-pocket film line. The film properties are listed in Table 2, which shows that the machine direction oriented, in-pocket films have similar MD and TD tensile properties as the high stalk films at the various draw ratios. The draw-down ratio of 11.3:1 is the maximum draw-down ratio limited by the orientation equipment and not the polymer film. The enhancements in tensile properties for examples 12-22 are similar to those discussed for examples 1-11.

EXAMPLES 23-30 Machine Direction Orientation of High density Films of Various Densities and MI₂

Three Equistar high density polyethylene resins, XL3805 (density: 0.940g/cm³, MI₂: 0.057 dg/rain, Mn: 18,000, Mw: 209,000), XL3810 (density: 0.940g/cm³, MI₂: 0.12 dg/min, Mn: 16,000, Mw: 175,000), L4907 (density: 0.949 g/cm³, MI₂: 0.075 dg/min, Mn: 14,300, Mw: 194,700), and L5005 (density: 0.949 g/cm³, MI₂: 0.057 dg/min, Mn: 12,600, Mw: 212,000) are converted into films of thickness of 6.0 mil by the high stalk process described in Examples 1-11 and the in-pocket' process described in examples 12-22. The blown films are then stretched in the machine direction. Listed in Table 3 are the machine direction and transverse direction tensile properties of each oriented film at their maximum draw-down ratios. The table shows that the tensile property enhancements depend on the density and MI₂ of the polyethylene resin, the blown film process, and maximum draw-down ratio of the MDO.

TABLE 1 Properties vs. Draw-down Ratio of High Density (0.959 g/cm³), High Stalk Films Properties in Machine Direction (MD) Properties in Transverse Direction (TD) Elon- Tensile Elon- Tensile Elongation Tensile Tensile Elongation Draw- gation strength gation strength @ break/ strength Elongation strength @ break/ Ex. down Modulus @ yield @ yield @ @ break elongation Modulus Elongation @ yield @ @ break elongation No. ratio psi % psi break % psi @ yield psi @ yield % psi break % psi @ yield 1 1:1 188,600 8.0 4,800 470 5,500 59 196,200 6.0 5,100 690 5,100 115 2 2:1 224,500 17 7,400 310 10,900 18 248,600 4.7 4,600 680 4,900 145 3 3:1 267,300 20 12,500 200 14,900 10 279,300 4.5 4,800 660 4,700 147 4 4:1 318,200 21 20,500 130 19,300 6 301,000 4.4 5,000 610 4,500 139 5 5:1 378,800 23 30,200 88 25,200 4 317,900 4.2 5,200 550 4,250 131 6 6:1 451,000 25 40,900 58 33,100 2.3 331,700 4.1 5,400 460 4,000 112 7 7:1 537,000 22 51,000 38 42,700 1.7 343,300 3.8 5,600 380 3,800 100 8 8:1 639,200 20 58,500 25 52,600 1.3 353,400 3.6 5,800 300 3,700 83 9 9:1 761,000 16 69,000 16 61,200 1 362,300 3.6 5,700 240 3,600 67 10 10:1  906,000 15 69,700 15 65,600 1 370,200 3.4 5,400 210 3,700 62 11 11:1  1,197,600 14 70,400 14 55,300 1 381,500 3.3 5,100 230 3,900 70

TABLE 2 Properties vs. Draw-down Ratio of High Density (0.959 g/cm³), In-pocket Films Properties in Machine Direction (MD) Properties in Transverse Direction (TD) Elon- Tensile Elon- Tensile Elongation Elon- Tensile Tensile Elongation Draw- gation strength gation strength @ break/ gation strength Elongation strength @ break/ Ex. down Modulus @ yield @ yield @ @ break elongation Modulus @ yield @ yield @ @ break elongation No. ratio psi % psi break % psi @ yield psi % psi break % psi @ yield 12 1:1 189,000 7.0 4,700 640 6,200 91 222,800 6.0 5,300 750 5,300 125 13 2:1 225,100 13 6,700 290 11,100 22 262,600 3.9 4,500 600 5,100 154 14 3:1 268,200 30 15,900 120 16,100 4.0 285,900 3.7 4,600 630 4,900 170 15 4:1 319,500 41 24,500 53 21,100 1.3 302,400 3.6 4,700 660 4,600 183 16 5:1 380,700 36 29,900 39 26,100 1.1 315,300 3.8 4,800 610 4,400 161 17 6:1 453,600 31 36,800 40 31,100 1.3 325,700 4.2 4,900 530 4,200 126 18 7:1 540,300 27 43,200 38 36,100 1.4 334,600 4.5 5,000 470 3,900 104 19 8:1 643,700 18 50,200 29 41,000 1.6 342,300 4.6 5,400 570 3,700 124 20 9:1 767,000 15 54,000 28 46,000 1.9 349,000 4.3 5,200 610 3,500 142 21 10:1  913,700 13 61,000 19 51,000 1.5 355,100 4.5 5,100 550 3,200 122 22 11.3:1   1,147,300 12 65,100 19 57,500 1.6 362,100 4.7 4,600 500 2,900 106

TABLE 3 Properties vs. Draw-down Ratio of High density Films of Various Densities and MI₂ Properties in Machine Direction (MD) Properties Transverse Direction (TD) MDO Elon- Tensile Elon- Tensile Elon- Tensile Elon- Tensile Resin Max. gation strength gation strength Elongation gation strength gation strength Elongation Properties Draw- @ @ @ @ @ break/ @ @ @ @ @ break/ Ex. Density MI₂ Film Down yield, yield, break, break, Elongation yield, yield, break, break, elongation No. g/cm³ dg/min Process Ratio % psi % psi @ yield % psi % psi @ yield 11 0.959 0.057 High Stalk 11.6:1 14 70,400 14 55,200 1 3.3 5,100 230 3,900 70 22 0.959 0.057 In-pocket 11.3:1 12 65,100 19 57,500 1.6 4.7 4,600 500 2,900 106 23 0.940 0.057 High Stalk  8.3:1 3 8,400 30 52,200 10 4 4,700 710 4,900 178 24 0.940 0.057 In-pocket  7.6:1 2 7,600 28 53,600 14 4 4,500 740 4,400 185 25 0.940 0.12 High Stalk  6.5:1 3 7,200 41 32,900 14 4 4,500 730 4,300 183 26 0.940 0.12 In-pocket  2.2:1 16 4,800 320 11,400 20 5 3,700 770 4,800 128 27 0.949 0.075 High Stalk 11.9:1 12 56,600 12 55,500 1 2.9 4,000 470 3,500 162 28 0.949 0.075 In-pocket  7.7:1 2 9,200 25 52,700 13 4 4,900 710 4,000 178 29 0.949 0.057 High Stalk 10.6:1 3 13,600 19 53,200 6 4 4,800 690 3,500 173 30 0.949 0.057 In-pocket 10.0:1 0 51,200 29 63,500 3 4 5,300 700 4,100 175 

1. (canceled)
 2. (canceled)
 3. (canceled)
 4. (canceled)
 5. (canceled)
 6. (canceled)
 7. (canceled)
 8. (canceled)
 9. (canceled)
 10. (canceled)
 11. (canceled)
 12. (canceled)
 13. (canceled)
 14. (canceled)
 15. (canceled)
 16. (canceled)
 17. (canceled)
 18. (canceled)
 19. A composition comprising: a high density polyethylene film having a draw-down ratio effective to give the film an MD tensile strength at yield greater than or equal to 50,000 psi, wherein the HDPE has a density greater than 0.940 g/cm³.
 20. The composition of claim 19 wherein the HDPE has a density greater than or equal to 0.949 g/cm³.
 21. The composition of claim 19 wherein the HDPE has a density within the range of 0.949 g/cm³ to 0.965 g/cm³.
 22. The composition of claim 19 wherein the HDPE has a density within the range of 0.949 g/cm³ to 0.959 g/cm³.
 23. The composition of claim 19 wherein the HDPE has a weight average molecular weight (Mw) within the range of 130,000 to 1,000,000.
 24. The composition of claim 23 wherein the Mw is within the range of 150,000 to 500,000.
 25. The composition of claim 23 wherein the Mw is within the range of 155,000 to 300,000.
 26. The composition of claim 23 wherein the Mw is within the range of 155,000 to 250,000.
 27. The composition of claim 19 wherein the HDPE has a number average molecular weight (Mn) within the range of 10,000 to 500,000.
 28. The composition of claim 27 wherein the Mn is within the range of 11,000 to 100,000.
 29. The composition of claim 27 wherein the Mn is within the range of 11,000 to 50,000.
 30. The composition of claim 27 wherein the Mn is within the range of 11,000 to 20,000.
 31. The composition of claim 19 wherein the draw-down ratio is greater than or equal to 10:1.
 32. The composition of claim 19 wherein the draw-down ratio is greater than or equal to 11:1.
 33. The composition of claim 19 wherein the MD tensile strength at yield is greater than about 55,000 psi.
 34. The composition of claim 19 wherein the film is oriented in the machine direction.
 35. The composition of claim 34 wherein the film has an elongation at break that is essentially the same as its elongation at yield. 